Wear Performance of Ceramic-On-Metal Hip Bearings

  • Jörn Reinders ,

    joern.reinders@med.uni-heidelberg.de

    Affiliation Laboratory of Biomechanics and Implant Research, Department of Orthopedics and Traumatology, Heidelberg University Hospital, Heidelberg, Germany

  • Robert Sonntag,

    Affiliation Laboratory of Biomechanics and Implant Research, Department of Orthopedics and Traumatology, Heidelberg University Hospital, Heidelberg, Germany

  • Christian Heisel,

    Affiliation Laboratory of Biomechanics and Implant Research, Department of Orthopedics and Traumatology, Heidelberg University Hospital, Heidelberg, Germany

  • Tobias Reiner,

    Affiliation Laboratory of Biomechanics and Implant Research, Department of Orthopedics and Traumatology, Heidelberg University Hospital, Heidelberg, Germany

  • Leo Vot,

    Affiliation Laboratory of Biomechanics and Implant Research, Department of Orthopedics and Traumatology, Heidelberg University Hospital, Heidelberg, Germany

  • Jan Philippe Kretzer

    Affiliation Laboratory of Biomechanics and Implant Research, Department of Orthopedics and Traumatology, Heidelberg University Hospital, Heidelberg, Germany

Abstract

Ceramic-on-metal (CoM) bearings are considered to be a promising alternative to polyethylene-based bearings or hard-on-hard bearings (Ceramic-on-Ceramic (CoC) and Metal-on-Metal (MoM)). Although, CoM shows lower wear rates than MoM, in-vitro wear testing of CoM shows widely varying results. This may be related to limitations of wear-measuring methods. Therefore, the aim of this study was to improve the gravimetric measurement technique and to test wear behaviour of CoM bearings compared to CoC bearings. Level walking according to ISO-14242 was simulated for four CoM and four CoC bearings. Prior to simulation, errors in measurement of gravimetric wear were detected and improvements in measurement technique incorporated. The results showed no differences in mean wear rates between CoM and CoC bearings. However, the CoM bearings showed wear results over a wide range of wear performance. High reliability of wear results was recorded for the CoC bearings. Material transfer was observed on the ceramic heads of the CoM bearings. Therefore, for level walking a partial mixed or boundary lubrication has to be assumed for this type of bearing. CoM is a highly sensitive wear-couple. The reasons for the observed behaviour cannot be clarified from this study. Simulator studies have to be considered as an ideal loading condition. Therefore, high variations in wear rates as seen in this study, even at low levels, may have an adverse effect on the in-vivo wear behavior. Careful clinical use may be advisable until the reasons for the variation are fully clarified and understood.

Introduction

Joint-related disorders of the hip such as persistent pain or functional disabilities can be successfully treated by total hip replacement (THR). Following register data, survival rates of approximately 90% after 10 years are reported [1]. However, the lifetime of an artificial joint is still limited and wear of the articulating surfaces remains a major limiting factor in this respect [2]. Nevertheless, expectations regarding quality of life and thus on implants are increasing [3]. The performance of implants therefore has to improve.

New-generation hard-on-hard bearings such as ceramic-on-ceramic (CoC) or metal-on-metal (MoM) are technically promising solutions for the wear problem. Currently, CoC is considered to be the gold-standard of a low-wearing bearing in THR with a decreased incidence of osteolysis [4]. However, breakage (rare incidence of 0-2% depending on the ceramics used [57]) and squeaking (incidence 0.5-20.9% [5,8]) of ceramic components are still a concern. For MoM, laboratory studies have shown low wear [9]. However, concerns exist regarding interaction of metal wear products with the immune system, which might take even place at low wear volumes [10]. In this context, cases of high-wear with local effects (metallosis, necrotic tissue, pseudotumours) [11,12] up to those showing massive-wear with systemic effects [12] have been reported and these have alarmed the orthopaedic community.

THR using a metallic liner and a ceramic head (CoM) has recently been introduced clinically to meet the aforementioned challenges. It is not known how many CoM bearings have been implanted to date. One study states that at least 10,000 CoM bearings have been implanted [13], but it is not clear how this number was derived. In fact, although CoM bearings are used clinically there is little knowledge about their in-vivo performance [14]. Some case reports have shown tremendous wear of CoM [15,16], but in those cases the technical design differed from that of modern CoM bearings. Keeping this in mind, simulator studies may be an important tool for acquiring knowledge of possible CoM-related risks.

Although some laboratory studies have shown low wear rates of CoM [1723], there is a high variance between the results of different research groups. Wear rates from published studies differ by a factor of 150 [17,20].

Possible reasons for this discrepancy are:

  • First, CoM is a highly sensitive wear-couple with widely ranging wear performance.
  • Second, the wear rate is generally low. Differences are due to limitations of the methods used to measure wear (mostly gravimetric).

The aim of this study was therefore to test the wear behaviour of CoM compared with CoC. To increase the validity of the results this study focused on improvements in the gravimetric measurements technique. The results are supported by continuous screening of the cobalt and chromium release, as important parameters for the clinical use.

Material and Methods

Simulator-study

For wear testing, four pairs of CoC bearings (Biolox®Delta, Ceramtec) and four pairs of CoM bearings (CoMplete, DePuy) with a nominal diameter of 36 mm were used. Wear tests were run on a single-station hip joint simulator (858 Mini Bionix II system; MTS Systems, Minnesota, USA). Level walking according to ISO 14242-1 was simulated. This includes a dynamic load up to 3 kN, a maximum flexion of 25° to 18° of extension, an adduction of 7° to 4° of abduction and an internal rotation of 2° to 10° of external rotation. Simulation was run to a total of 2.4 million cycles corresponding to approximately 1 year of use in an active patient [24]. Bovine serum with a protein content of 30 g/L was used as a substitute for synovial fluid. The simulation was interrupted every 200,000 cycles to clean and weigh the components. Every 400,000 cycles the bovine serum was completely changed.

Prior to simulation, CoC and CoM components were measured using a coordinate measuring machine (MarVision MS 222, Mahr, Göttingen, Germany; accuracy: ± 2.3 µm). Diameter and deviation of roundness of the heads and cups of both groups were determined. Subsequently the components were matched in order to achieve comparable clearances within both groups.

thumbnail
Figure 1. Relationship between weight determinations of two ceramic heads.

https://doi.org/10.1371/journal.pone.0073252.g001

Gravimetric repeatability, stability & disturbance reduction

For wear measurements, a high-precision balance (Genius ME 235S, Sartorius, Göttingen, Germany) with a specified repetitive accuracy of 25 µg was used. The repetitive accuracy specifies the accuracy of the measurement in the presence of identical physical conditions [25]. However, disturbances due to minimal changes of temperature, humidity and atmospheric pressure cannot be excluded even in a temperature-controlled room.

To characterise the system of gravimetric measurement used, two parameters were analysed: 1) The repeatability of a measurement system specifies variations in measurement under identical conditions (within one series of measurement) 2) The stability of a measurement system specifies differences of the mean value within a defined time interval (differences between measurement series).

Therefore the components (ceramic head, ceramic liner, metal liner) were measured in an own measurement series prior to simulation. Every series consisted of 10 measurement intervals during a time period of 30 days (stability analysis). Each of these 10 measurement intervals consisted of a gravimetric analysis (repeatability analysis) which was repeated for 12 times.

Determination of possible disturbances provides the opportunity for correction of measurement results. It was hypothesized that disturbing factors would act in the same way on identical measuring objects. To test this hypothesis, we performed an additional series of measurements on which two nearly identical (deviations only caused by production) components (two ceramic heads, two ceramic liners, two metal liners) were measured as described above.

Gravimetric analysis

The components were cleaned using mild detergents, ultrasonic baths and isopropanol in a repeating sequence. After the cleaning process the implants were vacuum-dried and tempered for at least 12 hours in a temperature-controlled precision measurement room. Each measurement was repeated 12 times. Calibrated control weights (Zwiebel, Saverne Cedex, France) were used as an additional reference during measurements. Volumetric wear was calculated based on the density of the ceramic (ρc = 4.37 mg/mm3) and the metal (ρm = 8.3 mg/mm3) components.

StabilityRepeatability
ComponentMeanMin.Max.DeviationSD max.
Ceramic head84.85418 g84.85395 g84.85434 g390 µg≤ 0.00002
Ceramic cup60.96731 g60.96713 g60.96743 g300 µg≤ 0.00002
Metal cup115.27250 g115.27243 g115.27253 g100 µg≤ 0.00002

Table 1. Gravimetrical determination of stability and repeatability of unused components.

CSV
Download CSV

Metal ion analysis

The simulations were run in a metal-free, low-contamination environment [26,27]. Fluid samples were taken every 200,000 cycles under clean room conditions. Cobalt and chromium content were analysed using high-resolution, inductively coupled mass spectroscopy (Element2; Thermo, Fisher Scientific, Bremen, Germany) according to previous published methods [26,27].

thumbnail
Figure 2. Volumetric wear of tested bearings (left: CoM; right: CoC).

Grey area: mean and range of lowest and highest wear couple.

https://doi.org/10.1371/journal.pone.0073252.g002

Statistics

The wear rates of both bearings were compared using Student’s t-test for two independent parametric samples with a level of significance set at p<0.05 (SPSS 16.0.1, SPSS Inc., Chicago, IL). All data are presented as mean ± standard deviation (SD).

Results

Gravimetric stability & repeatability, stability & disturbance reduction

Table 1 shows the results for stability and repeatability. High repeatability (deviation within one measurement) was found for every component. Stability, as a parameter for time-dependent differences in measurement results, shows differences of up to 390 µg for the ceramic head, but only 100 µg for the metal cup. Deviations can be defined as physical disturbances (changes in atmospheric pressure, temperature and humidity) [25] and these were found to be in wear-relevant ranges.

Significant correlations were observed between identical measuring objects for all pairings (Table 2, Figure 1). Generally, ceramics showed a better statistical relationship than metal cups did. However, the hypothesis that systematic disturbances can be detected by measuring nearly identical measuring objects was confirmed.

Correlation coefficientp value
Ceramic head0.937p ≤ 0.001
Ceramic cup0.930p ≤ 0.001
Metal cup0.772p = 0.009

Table 2. Statistical relationship between two identical measuring objects.

CSV
Download CSV

To compensate for these disturbances during wear simulation, physically and geometrically identical components (deviations ≤ 1%) were measured in parallel; based on this, a correction of the gravimetric results of the wear components was performed.

Simulation and gravimetric analysis

Clearance was lower for the CoC bearings (23.8 ± 3.1µm) than for CoM bearings (51.1 ± 2.0µm). Only small differences in deviations of roundness were observed (CoC: 5.49 ± 1.28µm; CoM: 4.84 ± 2.0µm)

No differences in wear rates (overall, running-in, steady state) were found between CoC and CoM (Table 3, Figure 2). However, wear rates of CoM bearings showed higher variations than CoC bearings. Overall the lowest and highest wear rates were observed for CoM bearings. The lowest wear rate for CoM was 0.017 mm3/106 cycles compared to 0.081 mm3/106 cycles for CoC. The highest wear rate of CoM was 0.212 mm3/106 cycles compared to 0.167 mm3/106 cycles for CoC.

Running-in wear in mm3/106 cyclesSteady-state wear in mm3/106 cyclesOverall wear in mm3/106 cycles
CoC0.163 ± 0.026 (0.137-0.199)0.038 ± 0.012 (0.027-0.055)0.118 ± 0.036 (0.081-0.167)
CoM0.134 ± 0.134 (-0.019-0.279)0.053 ± 0.038 (0.009-0.090)0.129 ± 0.096 (0.017-0.212)
p value0.6970.5710.851

Table 3. Mean, SD and range of wear rates of CoC and CoM bearings.

CSV
Download CSV
thumbnail
Figure 3. Head of CoM bearing (left) and CoC bearing (right).

https://doi.org/10.1371/journal.pone.0073252.g003

Wear of the CoC components was evenly distributed between heads (43.1 ± 9.2%) and inserts (56.9 ± 9.2%). For the CoM components wear was observed mainly on the metal inserts (97.2 ± 3.5%). Only marginal wear was observed on the ceramic heads (2.8 ± 3.5%).

Ceramic heads from the CoM bearings showed visible signs of metallic transfer in the form of stripes. For the ceramic heads of CoM bearings, the subjective amount of material transfer was higher for bearings with higher wear rates compared to the low-wearing CoM bearings. In comparison, no visible traces were found on the CoC heads (Figure 3).

Metal ion analysis

Results of ion-measurements are shown in Figure 4 for cobalt and chromium. As expected no ion-release of cobalt and chromium was observed for the CoC bearings. Additionally, these measurements confirm that no contamination occurred due to the simulator environment.

Measurements of the CoM bearings showed a continuous increase in the release of chromium and cobalt. By the end of the test 168 µg/L chromium and 331 µg/L cobalt had been released.

Discussion

Following successful improvement of the gravimetric measurement technique, this study compared the wear behaviour of the new CoM bearings to the gold-standard of CoC bearings. It has been shown that deviations in measurements (instability) occur over time, probably due to minimal changes in ambient conditions (intrinsic disturbances) [25]. These deviations were in wear-relevant ranges. By using equivalent reference heads and cups these disturbances can be reduced and the validity of measurement increased.

However, gravimetric measurements still exhibit limitations. A complete dismounting/mounting and cleaning are necessary. This might change the tribological system:

  • Wear influencing layers (e.g. tribolayer, phophatlayer etc.) may be removed [27,28].
  • With every mounting, components are macroscopically exactly aligned. Nevertheless, a correct alignment on a micron scale is technically difficult to realise. A slight component misalignment with an impact on wear cannot be excluded.
  • Incomplete cleaning and possible contamination cannot be excluded

Despite these limitations, gravimetric measurements are a highly important tool for determining wear. Additional information on the wear performance of implants can be provided by ion analytic measurements. Regarding ion exposure, a more continuous increase was detected without the variations that still exist in gravimetric measurements.

The mean wear of CoM and CoC bearings was comparable. However, a high variation was observed for CoM. The ratio between minimal and maximal wear was 12 for CoM and 2 for CoC.

In Figure 5 a box-and-whisker diagram shows differences between literature data regarding CoM simulator studies and the used control bearings (CoC & MoM). CoC bearings consistently show only small mean variations among different research groups. Wear results are also consistently low. These observations were confirmed in this study. The literature data confirm a characteristically wider range of wear for CoM than for CoC, and show that MoM bearings exhibit wear at a higher level and with greater variation than CoM bearings [1720,22,23].

Lubrication is assumed to be a key factor in the tribological performance of hard-on-hard bearings [29,30]. Simplified and theoretical models provide insights into possible fluid-film thicknesses and the predominant lubrication regimes. These models are based on material characteristics (clearance, roundness, roughness, material elasticity etc.), environmental characteristics (fluid viscosity) and activity characteristics (kinematics and kinetics) [31]. Regarding level walking (as simulated according to ISO 14242) these models indicate a mixed to fluid-film lubrication for MoM bearings and fluid-film lubrication for CoC bearings [32]. Although these models still display limitations [33,34], they have attained a high level of complexity and offer the possibility to predict in-vivo lubrication to a certain extent. In a recent study, Meng et al. [35] analysed the lubrication mode of hard-on-hard bearings including CoM bearings. They reported fluid-film lubrication for CoC during the whole gait cycle. A slightly inferior lubrication mode was found for CoM, with 80% of the gait cycle operating in the fluid-film mode. In the present study observation of metal transfer to the ceramic heads indicates a contact between both bearing partners.

thumbnail
Figure 4. Cumulative release of cobalt (left) and chromium (right).

https://doi.org/10.1371/journal.pone.0073252.g004

Only a few studies have been published on the clinical performance of CoM bearings [21,23,36]. Two of these [21,23] were follow-up studies from the same centre with different patient collectives, reporting results after 3 and 12 months [21] and 6 months [23] postoperatively. The median ion release of cobalt and chromium after 6 months showed no significant differences between CoM and MoM [23]. Significantly reduced median cobalt and chromium release was observed after 12 months [21]. Only a small number of patients were compared for CoM and MoM. Additionally, a relatively high number of outliers were excluded for both CoM (1 of 7 = 17% [23] and 4 of 22 = 18% [21]) and for MoM (1 of 7 = 17% [23] and 4 of 19 = 21% [21]). In a double-blinded randomized study, Schouten et al. [36] compared chromium and cobalt release in patients treated with CoM (n = 41) and MoM (n = 36) bearings and found no differences, after 6 and 12 months. At present, therefore, clinical follow-up shows no clear advantage of CoM bearings.

thumbnail
Figure 5. Literature data of CoM studies including control bearings (MoM and CoC)

https://doi.org/10.1371/journal.pone.0073252.g005

The clinical relevance of simulator studies is limited. The main limitation is the replication of one loading condition (walking) in a standardised system with matched bearings. In-vivo, multiple loading conditions occur, possibly resulting in different wear behaviours. Moreover, wear performance is potentially influenced by individual factors (alignment, synovial fluid, ligamental situation etc.).

In this context the introduction of microseparation [37] in simulator testing has been found to produce clinically relevant wear characteristics. To date, three simulator studies [23,38,39] have reported on the wear behaviour of CoM bearings under these tribologically adverse conditions. Lower wear than in MoM bearings is described in two of these studies [23,38]. In the third [39], CoM was analysed without a control group: higher absolute wear of CoM bearings was found than in the other two studies. The standard deviations [38,39] of the wear results were high, indicating considerable variance of wear.

We have not yet attained a full understanding of these complex in-vivo and in-vitro relationships. The excellent wear results of MoM in simulator studies have been confirmed only to a limited extent in the clinical situation. Some clinical trials have shown excellent long-term wear performance of MoM [14], but increasing numbers of studies have reported catastrophic results of MoM [12]. The reasons for this discrepancy have not yet been fully elucidated. With regard to the variation in wear behaviour of CoM, clinical follow-up studies are required to establish which patients may benefit from CoM bearings.

Conclusion

In this study CoM exhibited mean wear results as good as those for CoC. However, CoM is a highly sensitive wear-couple. The individual CoM bearings exhibit considerable variation in wear. Regarding the lubrication of CoM bearings, contact between bearing surfaces has been demonstrated and therefore a partial mixed or boundary lubrication has to be assumed. In contrast, CoC shows consistently low wear rates and therefore greater reliability. The reasons for these differences in behaviour require further clarification. Simulator studies such as ours have to be considered to provide ideal loading conditions with respect to matching of components, loading and alignment. Therefore, the high variation of wear in CoM seen in this study, even at low levels, may indicate potential problems with CoM bearings in-vivo. Caution in clinical use may be advisable until the reasons for the variations in wear are understood.

Author Contributions

Conceived and designed the experiments: JR CH JPK. Performed the experiments: JR LV RS. Analyzed the data: JR TR JPK. Wrote the manuscript: JR TR RS.

References

  1. 1. Labek G, Thaler M, Janda W, Agreiter M, Stöckl B (2011) Revision rates after total joint replacement: cumulative results from worldwide joint register datasets. J Bone Joint Surg Br 93: 293-297. PubMed: 21357948.
  2. 2. Garellick G, [!(surname)!] , Rogmark C, Herberts P (2009) Swedish hip arthroplasty register. In: Annual report Göteborg. Sahlgrenska University Hospital.
  3. 3. Kurtz S, Ong K, Lau E, Mowat F, Halpern M (2007) Projections of primary and revision hip and knee arthroplasty in the United States from 2005 to 2030. J Bone Joint Surg Am. 89: 780-785. doi:https://doi.org/10.2106/JBJS.F.00222. PubMed: 17403800.
  4. 4. D’Antonio J, Capello W, Manley M, Naughton M, Sutton K (2005) Alumina ceramic bearings for total hip arthroplasty: five-year results of a prospective randomized study. Clin Orthop Relat Res 436: 164-171. PubMed: 15995436.
  5. 5. Keurentjes JC, Kuipers RM, Wever DJ, Schreurs BW (2008) High incidence of squeaking in THAs with alumina ceramic-on-ceramic bearings. Clin Orthop Relat Res 466: 1438-1443. doi:https://doi.org/10.1007/s11999-008-0177-8. PubMed: 18299948.
  6. 6. Hannouche D, Nich C, Bizot P, Meunier A, Nizard R et al. (2003) Fractures of ceramic bearings: history and present status. Clin Orthop Relat Res 417: 19-26. PubMed: 14646699.
  7. 7. Willmann G. (2000) 2000 Ceramic femoral head retrieval data. Clin Orthop Relat Res 379: 22-28. doi:https://doi.org/10.1097/00003086-200010000-00004. PubMed: 11039788.
  8. 8. Walter WL, O’Toole GC, Walter WK, Ellis A, Zicat BA (2007) Squeaking in ceramic-on-ceramic hips: the importance of acetabular component orientation. J Arthroplasty. 22: 496-503. doi:https://doi.org/10.1016/j.arth.2006.06.018. PubMed: 17562404.
  9. 9. Kretzer JP, Kleinhans JA, Jakubowitz E, Thomsen M, Heisel C (2009) A meta-analysis of design- and manufacturing-related parameters influencing the wear behavior of metal-on-metal hip joint replacements. J Orthop Res 27: 1473-1480. doi:https://doi.org/10.1002/jor.20921. PubMed: 19472378.
  10. 10. Williams DH, Greidanus NV, Masri BA, Duncan CP, Garbuz DS (2011) Prevalence of pseudotumor in asymptomatic patients after metal-on-metal hip arthroplasty. J Bone Joint Surg Am. 93: 2164-2171. doi:https://doi.org/10.2106/JBJS.J.01884. PubMed: 22159851.
  11. 11. Kwon YM, Ostlere SJ, McLardy-Smith P, Athanasou NA, Gill HS et al. (2011) “Asymptomatic” pseudotumors after metal-on-metal hip resurfacing arthroplasty: prevalence and metal ion study. J Arthroplasty. 26: 511-518. doi:https://doi.org/10.1016/j.arth.2010.05.030. PubMed: 20591612.
  12. 12. Tower SS (2010) Arthroprosthetic cobaltism: neurological and cardiac manifestations in two patients with metal-on-metal arthroplasty: a case report. J Bone Joint Surg Am. 92: 2847-2851. doi:https://doi.org/10.2106/JBJS.J.00125. PubMed: 21037026.
  13. 13. Cigada A, Cotogno G, Chiesa R (2011) The ceramic-on-metal coupling in total hip replacements for young patients: a review study. J Appl Biomater Biomech 9: 2-10. PubMed: 21607934.
  14. 14. Zywiel MG, Sayeed SA, Johnson AJ, Schmalzried TP, Mont MA (2011) Survival of hard-on-hard bearings in total hip arthroplasty: a systematic review. Clin Orthop Relat Res 469: 1536-1546. doi:https://doi.org/10.1007/s11999-010-1658-0. PubMed: 21057988.
  15. 15. Steens W, Loehr JF, von Foerster G, Katzer A (2006) Chronic cobalt poisoning in endoprosthetic replacement. Orthopade 35: 860-864. doi:https://doi.org/10.1007/s00132-006-0973-3. PubMed: 16767456.
  16. 16. Valentí JR, Del Río J, Amillo S (2007) Catastrophic wear in a metal-on-ceramic total hip arthroplasty. J Arthroplasty. 22: 920-922. doi:https://doi.org/10.1016/j.arth.2006.06.008. PubMed: 17826286.
  17. 17. Affatato S, Spinelli M, Squarzoni S, Traina F, Toni A (2009) Mixing and matching in ceramic-on-metal hip arthroplasty: an in-vitro hip simulator study. J Biomech 42: 2439-2446. doi:https://doi.org/10.1016/j.jbiomech.2009.07.031. PubMed: 19758592.
  18. 18. Affatato S, Spinelli M, Zavalloni M, Traina F, Carmignato S et al. (2010) Ceramic-on-metal for total hip replacement: mixing and matching can lead to high wear. Artif Organs 34: 319-323. doi:https://doi.org/10.1111/j.1525-1594.2009.00854.x. PubMed: 20420614.
  19. 19. Barnes CL, DeBoer D, Corpe RS, Nambu S, Carroll M et al. (2008) Wear performance of large-diameter differential-hardness hip bearings. J Arthroplasty. 23: 56-60. doi:https://doi.org/10.1016/j.arth.2008.05.021. PubMed: 18722303.
  20. 20. Firkins PJ, Tipper JL, Ingham E, Stone MH, Farrar R et al. (2001) A novel low wearing differential hardness, ceramic-on-metal hip joint prosthesis. J Biomech 34: 1291-1298. doi:https://doi.org/10.1016/S0021-9290(01)00096-3. PubMed: 11522308.
  21. 21. Isaac GH, Brockett C, Breckon A, van der Jagt D, Williams S et al. (2009) Ceramic-on-metal bearings in total hip replacement: whole blood metal ion levels and analysis of retrieved components. J Bone Joint Surg Br 91: 1134-1141. PubMed: 19721036.
  22. 22. Ishida T, Clarke IC, Donaldson TK, Shirasu H, Shishido T et al. (2009) Comparing ceramic–metal to metal–metal total hip replacements—a simulator study of metal wear and ion release in 32- and 38-mm bearings. J Biomed Mater Res B Appl Biomater 91: 887-896. PubMed: 19598291.
  23. 23. Williams S, Schepers A, Isaac G, Hardaker C, Ingham E et al. (2007) The 2007 Otto Aufranc Award: Ceramic-on-metal hip arthroplasties: a comparative in vitro and in vivo study. Clin Orthop Relat Res 465: 23-32. PubMed: 18090468.
  24. 24. Kinkel S, Wollmerstedt N, Kleinhans JA, Hendrich C, Heisel C (2009) Patient activity after total hip arthroplasty declines with advancing age. Clin Orthop Relat Res 467: 2053-2058. doi:https://doi.org/10.1007/s11999-009-0756-3. PubMed: 19247729.
  25. 25. Pozivil M, Winiger W, Wunderli S, Meyer VR (2006) The influence of climate conditions on weighing results. Microchim Acta 154: 55-63. doi:https://doi.org/10.1007/s00604-005-0479-4.
  26. 26. Heisel C, Streich N, Krachler M, Jakubowitz E, Kretzer JP (2008) Characterization of the running-in period in total hip resurfacing arthroplasty: an in vivo and in vitro metal ion analysis. J Bone Joint Surg Am. 90: 125-133. doi:https://doi.org/10.2106/JBJS.H.00437. PubMed: 18676947.
  27. 27. Kretzer JP, Krachler M, Reinders J, Jakubowitz E, Thomsen M et al. (2010) Determination of low wear rates in metal-on-metal hip joint replacements based on ultra trace element analysis in simulator studies. Tribol Lett 37: 23-29. doi:https://doi.org/10.1007/s11249-009-9486-7.
  28. 28. Wimmer MA, Fischer A, Büscher R, Pourzal R, Sprecher C et al. (2010) Wear mechanisms in metal-on-metal bearings: the importance of tribochemical reaction layers. J Orthop Res 28: 436-443. PubMed: 19877285.
  29. 29. Fisher J, Jin Z, Tipper J, Stone M, Ingham E (2006) Tribology of Alternative Bearings. Clin Orthop Relat Res 453: 25-34. doi:https://doi.org/10.1097/01.blo.0000238871.07604.49. PubMed: 17016223.
  30. 30. Kamali A, Hussain A, Li C, Pamu J, Daniel J et al. (2010) Tribological performance of various CoCr microstructures in metal-on-metal bearings. J Bone Joint Surg Br 92: 717-725. PubMed: 20436012.
  31. 31. Fisher J, Dowson D (1991) Tribology of total artificial joints. Proc Inst Mech Eng H. 205: 73-79. doi:https://doi.org/10.1243/PIME_PROC_1991_205_153_02. PubMed: 1840723.
  32. 32. Jin ZM, Medley JB, Dowson D Fluid film lubrication in artificial hip joints. In: AA Lubrecht, D Dowson MPGD. Tribology Series Elsevier (2003): 237-256.
  33. 33. Fan J, Myant C, Underwood R, Cann P (2012) Synovial fluid lubrication of artificial joints: protein film formation and composition. Faraday Discuss 156: 69-85. doi:https://doi.org/10.1039/c2fd00129b. PubMed: 23285623.
  34. 34. Myant C, Underwood R, Fan J, Cann PM (2012) Lubrication of metal-on-metal hip joints: the effect of protein content and load on film formation and wear. J Mech Behav Biomed Mater. 6: 30-40. doi:https://doi.org/10.1016/j.jmbbm.2011.09.008. PubMed: 22301171.
  35. 35. Meng Q, Liu F, Fisher J, Jin Z (2013) Contact mechanics and lubrication analyses of ceramic-on-metal total hip replacements. Tribol Int 63: 51-60. doi:https://doi.org/10.1016/j.triboint.2012.02.012.
  36. 36. Schouten R, Malone AA, Tiffen C, Frampton CM, Hooper G (2012) A prospective, randomised controlled trial comparing ceramic-on-metal and metal-on-metal bearing surfaces in total hip replacement. J Bone Joint Surg Br 94: 1462-1467. PubMed: 23109623.
  37. 37. Nevelos J, Ingham E, Doyle C, Streicher R, Nevelos A, Walter W et al. (2000) Microseparation of the centers of alumina-alumina artificial hip joints during simulator testing produces clinically relevant wear rates and patterns. J Arthroplasty. 15: 793-795. doi:https://doi.org/10.1054/arth.2000.8100. PubMed: 11021457.
  38. 38. Williams S, Al-Hajjar M, Isaac GH, Fisher J (2013) Comparison of ceramic-on-metal and metal-on-metal hip prostheses under adverse conditions. J Biomed Mater Res B Appl Biomater 101: 770-775. PubMed: 23359608.
  39. 39. Williams SR, Wu JJ, Unsworth A, Khan I (2011) Wear and surface analysis of 38 mm ceramic-on-metal total hip replacements under standard and severe wear testing conditions. Proc Inst Mech Eng H. 225: 783-796. doi:https://doi.org/10.1177/09544054JEM1994. PubMed: 21922955.