Figures
Abstract
Nanomechanical properties of filamentous biopolymers, such as the persistence length, may be determined from two-dimensional images of molecules immobilized on surfaces. For a single filament in solution, two principal adsorption scenarios are possible. Both scenarios depend primarly on the interaction strength between the filament and the support: i) For interactions in the range of the thermal energy, the filament can freely equilibrate on the surface during adsorption; ii) For interactions much stronger than the thermal energy, the filament will be captured by the surface without having equilibrated. Such a ‘trapping’ mechanism leads to more condensed filament images and hence to a smaller value for the apparent persistence length. To understand the capture mechanism in more detail we have performed Brownian dynamics simulations of relatively short filaments by taking the two extreme scenarios into account. We then compared these ‘ideal’ adsorption scenarios with observed images of immobilized vimentin intermediate filaments on different surfaces. We found a good agreement between the contours of the deposited vimentin filaments on mica (‘ideal’ trapping) and on glass (‘ideal’ equilibrated) with our simulations. Based on these data, we have developed a strategy to reliably extract the persistence length of short worm-like chain fragments or network forming filaments with unknown polymer-surface interactions.
Citation: Mücke N, Klenin K, Kirmse R, Bussiek M, Herrmann H, Hafner M, et al. (2009) Filamentous Biopolymers on Surfaces: Atomic Force Microscopy Images Compared with Brownian Dynamics Simulation of Filament Deposition. PLoS ONE 4(11): e7756. https://doi.org/10.1371/journal.pone.0007756
Editor: Andreas Hofmann, Griffith University, Australia
Received: April 7, 2009; Accepted: September 30, 2009; Published: November 4, 2009
Copyright: © 2009 Mücke et al. This is an open-access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original author and source are credited.
Funding: The authors have no support or funding to report.
Competing interests: The authors have declared that no competing interests exist.
Introduction
The flexibility of filamentous biopolymers reflects important aspects of their biological function. Probably the most extensively studied example is the bending capability of DNA for its importance in the packaging of the genome into nucleosomes, the chromatin fiber and chromosomes [1], [2]. Studies of the properties for many other filamentous biopolymers have been somewhat in the shadow of the DNA work, but they are using principally very similar concepts. The elasticity of cytoskeleton constituents such as actin filaments, microtubules, and intermediate filaments (IFs) determines the shape and mechanical properties of the cell. While the implication of the nanomechanical properties of IF proteins for their biological functions has been realized in many cases (for review see e.g. [3], these properties are only beginning to be understood.
One fundamental parameter that characterizes the conformation of a long polymer is its bending rigidity, which will determine how stiff the polymer behaves against external forces. The bending rigidity is generally expressed as the persistence length Lp. This is the length after which the chain “loses memory” of its initial direction due to thermal fluctuations. For instance, actin filaments have a persistence length of approx. 10 to 20 µm, for microtubules it is 300-fold higher [4]. The persistence length of vimentin IFs is about 20 times lower [5]. To measure the persistence length of vimentin IFs, we employed atomic force microscopy (AFM). In this procedure [5], it was necessary to find conditions for the binding of vimentin filaments to the support that allowed the filament to equilibrate on the surface. The distinction between conditions of surface equilibration (SE) and surface trapping (ST) presented an important challenge for the interpretation of AFM data.
Here we compare quantitative evaluations of AFM images taken under different conditions of filament-surface interaction with computer simulations of the polymer deposition. We demonstrate that it is possible to distinguish between SE and ST conditions, even if the bending flexibility of the filament is not known a priori.
Theoretical considerations
The persistence length LP of a polymer chain is defined as the correlation length of the direction of the chain measured along its contour in three dimensions [6], [7] (1)
Here is the unit tangent vector of the chain; s and s+s′ the positions along the chain contour. The angular brackets indicate the thermal average over all positions and chain conformations. Molecules shorter than Lp behave approximately like a rigid rod, while longer chains show significant internal flexibility.
The bending elasticity A - the energy required to bend a polymer segment of unit length over an angle of one radian - is related to the persistence length by LP = A/kBT, kB being the Boltzmann's constant and T the absolute temperature. The energy required to bend two segments of the chain of length l by an angle Θ with respect to one another is [6](2)
The persistence length of a polymer chain can be determined from eq. (1), averaging over a large number of chain contours. Many studies have used two-dimensional images of polymer chains on surfaces for determining their bending elasticity or permanent bending, e.g. for DNA molecules imaged by electron (EM) [8] or atomic force microscopy (AFM) [9]–[12], or for intermediate filaments imaged by AFM [5], [13], [14]. In all of these cases some assumptions must be made as regards the relation between the three-dimensional structure of a polymer chain and its two-dimensional image, which strongly depends on the polymer-surface interaction. Two extreme cases have generally been considered: i) two-dimensional equilibration, where the polymer chain interacts rather weakly with the surface and can relax to a two-dimensional equilibrium conformation, and ii) so-called ‘trapping’ where the polymer binds irreversibly to the surface, starting at a few contact points from where complete adsorption is propagated.
In the first case, when the polymer conformation is equilibrated in two dimensions, the adsorbed polymer can be treated with exactly the same formalism as the one moving free in solution, except that the chain is confined to one plane. In the case of trapping, i.e. strong polymer-surface interaction, it is generally assumed that the chain conformation on the surface is a projection of its three-dimensional conformation to the plane. This model proved particularly useful for long polymer chains [5], [9], [10], [15]. However, this approximation is too simplistic to understand the chain deposition process in detail, since significant conformational changes can occur after the chain has made contact with the surface. Thus, numerical simulations need to be done and compared with experiments performed with polymer chains of various lengths. This may allow us to connect the two-dimensional (2D) conformation of a polymer chain trapped on a surface reliably with its three-dimensional (3D) structure free in solution. Since the interaction with the surface is assumed to be very strong, its details do not influence the final conformation of the chain on the surface. This offers the advantage that fundamental physical properties of the polymer such as its persistence length can be obtained without regarding the details of surface interaction, in contrast to a scenario where some surface mobility is encountered.
Strong biopolymer surface interactions have already been observed and analyzed [5], [9], [10], [15]. For long three-dimensional chains and strong surface interactions a 3D-to-2D projection model was assumed and a broad distribution of the calculated mean-square end-to-end-distances for long DNA-fragments was reported [9], [10]. In earlier work [5], we used the same model but for shorter fragments with a broad distribution of contour lengths. The persistence length calculated in that work for longer segments of about 3LP gave results comparable with filaments which were allowed to equilibrate on the surface. In contrast, for short segments the calculations failed. Consequently, a more detailed analysis was indispensable. Here we now develop a model that describes ideal trapping conditions for the whole chain.
We performed Brownian dynamics simulations of flexible chain deposition onto a flat surface and compared the resulting chain conformations with experimental data gathered on vimentin filaments with AFM. The procedure that we report here enables us to predict the 3D conformational properties even of short chains (at or below the persistence length) from the 2D images.
Brownian Dynamics simulations
Brownian Dynamics (BD) simulations were done with corchy++, a BD and Monte-Carlo simulation package for linear and circular worm-like chains (WLC) described in earlier publications [16], [17]. The polymer was approximated by a chain of beads connected through straight elastic segments, each of which carried a local reference frame. The energy of the system was given by harmonic potentials with respect to: (i) the angles between consecutive segments, (ii) the twist angles between consecutive reference frames, and (iii) the deviations from the equilibrium segment length. Excluded-volume or other long range intra-chain interactions were neglected, which is justified for these chains lengths according to the theory developed by Yamakawa and Stockmayer [[18]]. Each step in the BD trajectory was performed according to the algorithm of Ermak and McCammon [19] with second order corrections [20]. The hydrodynamic interactions between the beads were given by the Rotne-Prager tensor [21]. The initial polymer conformation was obtained by a Monte Carlo procedure, in which the polymer was represented as a linear chain of straight segments with a fixed length. The energy parameters were the same as in the BD model. A trial Monte Carlo step was performed by, subdividing the chain into two parts at a random joint, and one of the parts was rotated about a random axis that passed through this joint. The angle of rotation was uniformly distributed in an interval (-Θ,Θ), where Θ was chosen in such a way that the acceptance rate was approximately 50%. The steps were accepted or rejected according to the classical Metropolis criterion. Monte Carlo steps were done successively until the chains reached the mean-square end-to-end distance expected for a relaxed chain.
This initialized conformation was relaxed in the BD force field to match the equilibrium distribution over the segment lengths. Trapping on a surface (ST) was modeled in the following way. The position of the surface was assumed to be at the horizontal plane z = 0. At t = 0, the chain was positioned in space so that its lowest joint lay at the trapping surface. Whenever during the simulation any other joint passed through the surface, its z-coordinate was set to 0 and its position became fixed for the rest of the simulation run. The simulation continued until all the joints were fixed. The hydrodynamic interactions between the chain and the surface were neglected. In the case of ‘weak’ interaction (SE), the same procedure was applied with the exception that only the z-coordinate of the trapped joints became fixed, while 2D movement was still allowed.
For historical reasons, we used parameters corresponding to double helical B-DNA. Since the length scale is taken relative to the persistence length, this can easily be rescaled for other WLC. Thus, the persistence length for B-DNA was LP = 50 nm, the equilibrium segment length l0 = 1.67 nm (30 segments per one persistence length), and the total length of the chain L = 200 nm = 4LP. For modeling the hydrodynamic radius, each 1.67 nm segment was covered with a bead of radius rb = 1.33 nm (so that the neighboring beads were overlapping). The simulation time step was Δt = 20 ps, the torsional rigidity C = 2.5⋅10−19 erg cm, the temperature T = 298 K. The elastic stretching modulus was arbitrarily chosen to be 250 pN, in order to provide reasonable computational time.
Materials and Methods
Preparation of intermediate filaments
The cloning and expression of recombinant human vimentin was done as described [22]–[24]. The stepwise dialysis of proteins into low salt buffers and subsequent assembly experiments were done as described [5].
Atomic force microscopy
Assembled filaments were deposited onto glass modified to be hydrophilic or freshly cleaved mica in 2 mM sodium phosphate, pH 7.5, 100 mM KCl [13], [25] (phosphate assembly buffer). The experimental setup has been reported previously [5]. Vimentin was assembled in phosphate assembly buffer at 0.2 mg/ml for about 25 min. Then, the sample was diluted 40 to 60 fold in the same buffer and applied to the surface. We use 100 µm long cantilevers with oxide sharpened silicon nitride tips (type NP-S from Digital Instruments, Santa Barbara, USA). All AFM image were recorded in tapping-mode using Nanoscope IIIa running with software version 5.12r3 (Digital instruments, Santa Barbara, USA) [5].
Image processing
Using the Nanoscope III software, the images were flattened and zoomed to a pixel size of about 1∶50 of the estimated persistence length of the filaments using the software supplied with the AFM (Nanoscope ver. 512r3, Veeco Santa Barbara CA). These images were opened and scaled in ImageJ V1.31v (National Institutes of Health, USA; freely downloadable from http://rsb.info.nih.gov/ij). Filament contours were traced using the “freehand line tool” and exported as XY-coordinate sets. The exported contours were smoothed using the weighted average of five contiguous XY-coordinates centered around a given XY-coordinate, thus minimizing the errors due to the discretized contours [5]. Each smoothed backbone was split into segments of increasing contour lengths in 0.1 µm increments. For each segment length s, the mean cosine of the angle between the initial and final directions (equation 4), the mean-square angle (equation 5), the normalized mean fourth power of the angle (equation 6) and the mean-square end-to-end distance (equation 7) were computed [8]. The normalized autocorrelation function was calculated by equation 8. Curve fitting was done in Origin 7.0 (OriginLabs Corp, MA, USA).
Data analysis
The equations used were derived in [8], [10], and summarized in [5]. In brief:
The normalized probability distribution function in two dimensions for the filament bending angle Θ between segments of the polymer separated by a contour distance s is Gaussian and can be written as: (3)
The distribution function can be used to determine the persistence length from the average cosine of the angle Θ between tangent vectors of the polymer:(4)
The ratio of the contour distance s to the persistence length equals the mean–square bending angle:(5)
The mean-fourth power of the angle, as a statistical test of Gaussian distribution, is:(6)
The mean-square end-to-end distance on a two-dimensional surface as a function of contour distance s depends on the persistence length LP according to Rivetti et al.[10]: (7)
The normalized correlation function of the bending angle Θ along the contour is computed as:(8)
Results
AFM images versus Brownian dynamics simulation of IFs adsorbed to different surfaces
A schematic view of the deposition process simulated by the BD model is shown in Fig. 1 and 2. Two scenarios have been simulated: Fig. 1a illustrates the case of strong chain-surface interactions (ST) and Fig. 1b the case of weak interactions (SE). QuickTime movies of the two simulations are available in the supplement (Movie S1, S2).
Filaments were first equilibrated in 3D. Left images illustrate the case of strong chain-surface interaction. Right images illustrate the case of weak chain-surface interaction. The upper images show the point of first contact between chain and surface (time 0 ms). The middle images show snapshots during the deposition process (time: 2 ms left image; 4 ms right image). The lower images show conformations of the fully adsorbed chains (time about 8 ms).
The contour lengths of the simulated chains was set to 4 x LP and of the IFs 3 x to 7 x LP, respectively. Brownian dynamic simulations were performed for weak (a) and strong (b) filament surface interaction. If weak filament surface interaction was taken into account smooth contours with random bending can be observed (a). If strong filament surface interactions were taken into account (b) loops can be found and the curvature does not appear random. Traced vimentin IF contours deposited on modified glass (c) and freshly cleaved mica (d) are shown. After image processing (see Material and Methods), representative contours have been selected and arranged in an image. Image size: 10 x LP.
A first qualitative comparison of the adsorbed 2D conformations after the two different deposition scenarios, using simulated and AFM-measured contours, is shown in Fig. 2. For better presentation, the scale of each plot is set to ten times the persistence length. In Fig. 2a outlines of the simulated fibers in the limit of SE are presented; Fig. 2c shows outlines of AFM images of vimentin filaments on a glass surface, where rearrangements occur after adsorption. Qualitatively, both images show similar, random conformations, suggesting that the vimentin filaments may be represented by a WLC-model. Fig. 2b shows BD-simulated contours for the case of ST. Correspondingly, outlines of AFM images of vimentin filaments on mica are shown in Fig. 2d. Again, the simulation and the experiment are qualitatively similar and clearly different from the filaments that can rearrange after deposition. Typically, loops can be found in the case of ST, and the filaments show stretches of rather uniform curvature. Sometimes long straight segments can be found followed by a narrow curve or loop. From these data one might expect that the Gaussian distribution of bending angles, which governs the WLC statistics of a homogeneous elastic polymer, is lost.
Quantitative comparison of AFM images as BD-simulated chains under surface equilibrium and trapping conditions
To extract parameters that can be used to compare the fibers quantitatively, we plotted the cosine of the mean-angle, the fourth moment, the mean-square angle and the mean-square end-to-end distance against the filament contour length, and fitted these data with the equations given in the theory part. The results are shown in Table 1, 2 and Fig. 3. For visual comparison the experimental and the simulation results were merged (Figure S1). As a first general result, it is evident that all curves, including the trapped ones, can be fitted with the 2D equations. Moreover, the fourth moment of the distribution is about or more than 3, still indicating a Gaussian distribution for each deposition scenario. Only, for the mean-square angle calculation, the fit deviated systematically. Here the lowest apparent persistence length was obtained (see below).
Data points are calculated from the contours (black, simulated SE; red, simulated ST; blue, vimentin on glass; red vimentin on mica). Each data set was then fitted by the equations on the right column (straight lines). The fitting results are further described in Tab. 1.
Trapping phenomena obtained by Vimentin imaging
In the case of SE, the obtained mean value for the persistence length of vimentin LP (<cos(Θ)>, <Θ2> and <R2>) is 1050 nm (Range: 980–1100 nm). In contrast to these values, the mean LP in the case of ST is 326 nm (Range: 180–445 nm) (see Tab. 1). The observed range of the LP values in the case of SE (as expected for a WLC) is independent of the filament length and the equation used. However, in the case of ST a strong dependence of the LP(Θ2) and LP(R2) of the filament lengths was measured. Hence, one may ask whether the trapping scenario observed is ideal or not, in the sense that some movement on the surface after adsorption is still possible. Dependence of the calculated persistence length on filament length was not observed with the values of LP(cos(Θ)). For long chains the lowest LP(Θ2) was measured, i.e. 180 nm. This is only 17% of the LP obtained in the case of SE. To understand this type of capture mechanism in more detail we performed BD simulations to mimic the ideal trapping scenario.
The ideal trapping phenomena observed by BD simulations
Ideal trapping absorption phenomena (ST) were simulated on sets of 2000 filaments for three different filaments lengths. All calculated values for the apparent persistence length of adsorbed filaments with different contour lengths exhibit the same trend: the shorter the filaments, the higher the observed apparent persistence length (Tab. 2, Fig. 4). Interestingly, LP(Θ2) is much lower than compared to the other calculated persistence lengths. For filament lengths of 4LP only 20% of the LP was calculated. This behavior is comparable to that of vimentin filaments on mica (17% of the LP).
The normalized LP (R2) (values see Tab. 2, right column) are plotted versus the normalized filament lengths (squares, vimentin filaments adsorbed on mica; circles, simulated filaments (ST)).
Normalized correlation function of the bending along the outlines
To get a robust criterion for the filament-surface interaction scenario we decided to analyze the correlation of the bending direction along the contour (Materials and Methods, eq. 7). For a kinetically trapped WLC a characteristic feature is the presence of loops due to self crossings. In fact, many loops were found in the ideal trapping scenario at contour lengths of about 4LP. A loop is a conformation where the direction of the bending is correlated over a certain distance. In contrast, for an equilibrated WLC (SE) one major assumption is that the direction of the bending is not correlated. Therefore, in an ideal equilibrated scenario the theoretical value for the correlation of the bending direction is zero for all segment lengths. For the trapping scenario 2000 deposition processes were simulated with filament lengths ranging from LP to 4LP.
The normalized correlation function for the 4LP filaments exhibits values of 0.05 to 0.12 for normalized segment lengths in the range of 0.75<(s/LP(Θ2))<2.0 (Fig. 5). For very short segment lengths of the filaments, s<0.75 LP(Θ2), the measured and the simulated curves differed significantly (Fig. 5). In that range, the deviation is due to the discretization of the contours and the subsequent smoothing. Consequently this range was excluded from the integration. The value of the integral over the range of normalized segment lengths range is 0.10 (Tab. 2) for the 4LP filaments. For filament lengths in the range of LP a lower integral value of 0.02 was obtained. The kinetically trapped vimentin filaments exhibited comparable integral values. For the long filaments (3.9LP) the observed integral is 0.12 and 0.02 for the short filaments.
The mean length of measured trapped filaments (open squares) was 1 x LP (dark grey) and 4 x LP (light grey). Filaments with lengths of about 4 x LP adsorbed on glass (black squares) exhibited no systematic error compared to the theoretical value for equilibrated filaments of 0 (black line). The simulated filaments exhibit a correlation of the curvature by ST (line, light grey). The same correlation is obtained for vimentin filaments adsorbed on mica.
Discussion
We have analyzed the conformation of vimentin filaments on surfaces by atomic force microscopy (AFM), using adsorption conditions for near-ideal surface equilibration (SE) or surface trapping (ST). SE conditions imply that the interaction with the surface is strong enough to bind the molecule to the AFM support, but weak enough to allow sliding on the surface and adaptation of a two-dimensional equilibrium conformation. ST conditions, on the other hand, prevail when the interaction with the surface is strong enough to prevent an adsorbed part of the molecule from moving further; in that case, the conformation on the surface is close to a two-dimensional projection of the three-dimensional solution conformation.
These two adsorption conditions, SE and ST, were used in Brownian dynamics simulations of the deposition of flexible polymer chains on a surface. The apparent polymer flexibility, expressed as a persistence length, was then calculated from both the experimental and the theoretical data sets using three different procedures as described above: calculation from the mean-square end-to-end distance as function of contour length, from the decay of the average cosine of the bending angle with the contour length, and from the mean-square bending angle as a function of contour length. Under SE conditions all three procedures gave the same value of about 1 µm for vimentin IFs. ST conditions consistently led to a reduced apparent persistence length, with a ratio of LP(ST)/LP(SE) decreasing from 0.45 for the shortest contour lengths (LP) to the theoretical value of 0.3 for long contour lengths (4LP). These ratios were obtained both for the data from AFM images and the simulated polymer contours (Fig. 4).
We conclude that neither the three methods used to analyze the imaged contours nor a comparison between them can distinguish between different adsorption scenarios without prior knowledge of the true value of the persistence length. However, trapping leads to a visible increase in the number of ‘looped’ conformations where the filament is bent into the same direction over long stretches. This tendency to keep the bending direction can be quantified by computing the autocorrelation function of the bending angle (Fig. 5). Trapped chains exhibit a non-zero value of this function over a large range of contour lengths, both in the simulated and in the experimental data. For surface-equilibrated chains, the theoretical value of this function is zero, which is in complete agreement with the experimental data. In addition, calculation of the apparent LP(Θ2) and LP(R2) can be used to detect the adsorption mechanism. In the case of ‘ideal SE’, LP(Θ2) and LP(R2), give similar results, whereas LP(Θ2) will be significant lower than LP(R2) in the case of trapping (since trapping results in tighter bending on the average, this difference may be partly due to the fact that eq. 5 is an approximation for the limit of small bending angles). This latter strategy allows one to determine the adsorption scenario beforehand and then to select the appropriate equation for obtaining the value of the persistence length.
Supporting Information
Figure S1.
Comparison (overlay) of the quantitative analysis of the simulated (lines) and the traced contours from AFM images (squares). Data were taken from Fig. 3. The equilibrated filaments (black) and the trapped filaments (gray) show very good agreement.
https://doi.org/10.1371/journal.pone.0007756.s001
(4.25 MB DOC)
Movie S1.
Brownian dynamics simulation of chain deposition with surface equilibration (see text)
https://doi.org/10.1371/journal.pone.0007756.s002
(16.21 MB MPG)
Movie S2.
Brownian dynamics simulation of chain deposition with surface trapping (see text)
https://doi.org/10.1371/journal.pone.0007756.s003
(15.61 MB MPG)
Acknowledgments
We would like to thank Ueli Aebi and Laurent Kreplak for the interesting and helpful discussions.
Author Contributions
Conceived and designed the experiments: NM RK HH MH JL. Performed the experiments: NM RK MB. Analyzed the data: NM KVK RK MB HH JL. Contributed reagents/materials/analysis tools: HH. Wrote the paper: NM KVK RK MB HH MH JL.
Reference
- 1. Garcia HG, Grayson P, Han L, Inamdar M, Kondev J, et al. (2007) Biological consequences of tightly bent DNA: the other life of a macromolecular celebrity. Biopolymers 85: 115–130. 10.1002/bip.20627 [doi].
- 2. Langowski J, Schiessel H (2004) Theory and computational modeling of the 30 nm chromatin fiber. Chromatin Structure and Dynamics: State-of-the-Art Amsterdam: Elsevier 397–420.
- 3. Herrmann H, Hesse M, Reichenzeller M, Aebi U, Magin TM (2003) Functional complexity of intermediate filament cytoskeletons: from structure to assembly to gene ablation. Int Rev Cytol 223: 83–175.
- 4. Gittes F, Mickey B, Nettleton J, Howard J (1993) Flexural rigidity of microtubules and actin filaments measured from thermal fluctuations in shape. J Cell Biol 120: 923–934.
- 5. Mücke N, Kreplak L, Kirmse R, Wedig T, Herrmann H, et al. (2004) Assessing the flexibility of intermediate filaments by atomic force microscopy. J Mol Biol 335: 1241–1250.
- 6. Landau LD, Lifshitz EM (1986) Theory of Elasticity.Oxford: Pergamon Press.
- 7. Kratky O, Porod G (1949) Röntgenuntersuchung gelöster Fadenmoleküle. Rec Trav Chim 68: 1106–1113.
- 8. Frontali C, Dore E, Ferrauto A, Gratton E, Bettini A, et al. (1979) An absolute method for the determination of the persistence length of native DNA from electron micrographs. Biopolymers 18: 1353–1373.
- 9. Bussiek M, Mücke N, Langowski J (2003) Polylysine-coated mica can be used to observe systematic changes in the supercoiled DNA conformation by scanning force microscopy in solution. Nucleic Acids Res 31: e137.
- 10. Rivetti C, Guthold M, Bustamante C (1996) Scanning force microscopy of DNA deposited onto mica: equilibration versus kinetic trapping studied by statistical polymer chain analysis. J Mol Biol 264: 919–932.
- 11. Schulz A, Mücke N, Langowski J, Rippe K (1998) Scanning force microscopy of Escherichia coli RNA polymerase.sigma54 holoenzyme complexes with DNA in buffer and in air. J Mol Biol 283: 821–836.
- 12. Wiggins PA, van der Heijden T, Moreno-Herrero F, Spakowitz A, Phillips R, et al. (2006) High flexibility of DNA on short length scales probed by atomic force microscopy. Nat Nanotechnol 1: 137–141. nnano.2006.63 [pii];10.1038/nnano.2006.63 [doi].
- 13. Mücke N, Kirmse R, Wedig T, Leterrier JF, Kreplak L (2005) Investigation of the morphology of intermediate filaments adsorbed to different solid supports. J Struct Biol 150: 268–276.
- 14. Wickert U, Mücke N, Wedig T, Müller SA, Aebi U, et al. (2005) Characterization of the in vitro co-assembly process of the intermediate filament proteins vimentin and desmin: mixed polymers at all stages of assembly. Eur J Cell Biol 84: 379–391.
- 15. Sushko ML, Shluger AL, Rivetti C (2006) Simple model for DNA adsorption onto a mica surface in 1:1 and 2:1 electrolyte solutions. Langmuir 22.
- 16. Klenin K, Merlitz H, Langowski J (1998) A Brownian dynamics program for the simulation of linear and circular DNA and other wormlike chain polyelectrolytes. Biophys J 74: 780–788. S0006-3495(98)74003-2 [pii];10.1016/S0006-3495(98)74003-2 [doi].
- 17. Merlitz H, Rippe K, Klenin KV, Langowski J (1998) Looping dynamics of linear DNA molecules and the effect of DNA curvature: a study by Brownian dynamics simulation. Biophys J 74: 773–779. S0006-3495(98)74002-0 [pii];10.1016/S0006-3495(98)74002-0 [doi].
- 18. Yamakawa H, Stockmayer WH (1972) Statistical Mechanics of Wormlike Chains.2. Excluded Volume Effects. Journal of Chemical Physics 57: 2843–&.
- 19. Ermak DL, McCammon JA (1978) Brownian dynamics with hydrodynamic interactions. Chemical Physics 69: 1352–1359.
- 20. Iniesta A, Garcia de la Torre J (1990) A second-order algotithm for the simulation of the Brownian dynamics of macromolecular models. J Chem Phys 92: 2015–2018.
- 21. Rotne J, Prager S (1969) Variational treatment of hydrodynamic interaction in polymer. Chemical Physics 50: 4831–4837.
- 22. Herrmann H, Hofmann I, Franke WW (1992) Identification of a nonapeptide motif in the vimentin head domain involved in intermediate filament assembly. J Mol Biol 223: 637–650.
- 23. Herrmann H, Haner M, Brettel M, Müller SA, Goldie KN, et al. (1996) Structure and assembly properties of the intermediate filament protein vimentin: the role of its head, rod and tail domains. J Mol Biol 264: 933–953.
- 24. Herrmann H, Haner M, Brettel M, Ku NO, Aebi U (1999) Characterization of distinct early assembly units of different intermediate filament proteins. J Mol Biol 286: 1403–1420.
- 25. Mücke N, Wedig T, Bürer A, Marekov LN, Langowski J, et al. (2004) Molecular and biophysical characterization of assembly-starter units of human vimentin. J Mol Biol 340: 97–114.